The occurrence of fretting corrosion on nominally fixed surfaces of high-loaded parts of mining machines and mechanisms is considered. Examples of wear and damage of critical parts, bearing assemblies of engines of dump trucks in fretting conditions are given. The mechanisms of fretting corrosion when using wear-resistant coatings are considered. It is noted that when choosing protective thin-layer coatings that provide an increase in the fretting-resistance of surfaces of tightly contacting parts, it is necessary to take into account both their wear resistance and the ability to resist shear. At the same time, the thickness of such coatings allows preserving, during operation, those provided during the assembly of the tension, without disturbing the maintainability of the nodes. The results of research of fretting wear of a number of coatings on a special installation are given. The mechanisms of wear of a number of thin-layer coatings based on friction-mechanical brazing, polymer fluorocarbon composition, solid lubricant coating using scanning electron microscopy were studied. Recommendations on the use of the studied thin-layer coatings for high-loaded parts of mining machines operating in fretting corrosion conditions have been developed. The aim of the work was to study the effect of a number of thin-layer coatings on the wear of highly loaded connections of the mechanisms of mining machines, in particular bearing assemblies of quarry dump trucks operating under fretting corrosion conditions.
The main trend in the development of modern diesel engine manufacturign is the creation of high-powered, reliable and economical internal combustion engines (ICE), which are widely used in various industries, including mining machinery. The application of the methods of gas-thermal and gas-plasma coating for obtaining wear-resistant layers on piston rings for large internal combustion engines of quarry transport – diesel locomotives and dump trucks- is considered. It is shown that the abrasive-jet machining of base coat is widely used as a preparatory operation before coating process, and the roughness of the working surface of the rings after abrasive-jet machining has a significant impact on the adhesion strength of the coating with the base material. The selection of the surface roughness and the conditions of abrasive-jet machining for increasing the coating adhesion strength to the base coat significantly determines both the thickness of the coating and the reliability of the part itself. The aim of the paper is to investigate the dependence of the adhesion strength of a gas-thermal wear-resistant coating of piston rings of large engines of quarry transport, including dump trucks and diesel locomotives, from the roughness of the working surface after abrasive-jet machining, which in turn depends on its modes (distance to the nozzle exit section, the number of passes, the working air pressure, the shot change rate). The working surface adhesion strength of piston rings with diameter of 210 mm coated with molybdenum and steel wire composition was investigated by the twisting angle at which the coating peeled. It is shown that the roughness providing a twist angle greater than 35° should be more than 22 μm, which does not cause coating peeling off. Modes of abrasive-jet machining providing the specified values of roughness: working air pressure is 0.4 MPa, distance to the nozzle exit section is 110 mm, the number of passes is 2, and the shot changes after processing 40 mandrels.
The paper considers the application of polymer composite materials in friction units of downhole oil pumps. The proposed scheme test samples of various composite materials paired with a steel roller adopted by the size of the spots wear using the criterion of resistance. As it is shown significant influence on the wear resistance of the friction pair, working in the crude oil environment, has not only the composition but also the reinforcing fibers direction. The best re-sults were obtained for a sample of polyamide reinforced with 50 % of high molecular weight synthetic fibers placed perpendicular to the friction surface.
