2411-3336 2541-9404 Записки Горного института Journal of Mining Institute Санкт-Петербургский горный университет императрицы Екатерины ΙΙ Empress Catherine II Saint Petersburg Mining University pmi-15312 https://pmi.spmi.ru/pmi/article/view/15312 Статьи Articles Electrolytic deposition of molybdenum Электролитическое осаждение молибдена Porfirov P. P. Порфиров П. П. Porfirov P. P. pmi@spmi.ru (Россия) (Russia) 01 01 1935 1935 9 1 35 39 07 07 1934 03 09 1934 01 01 1935 © 1935 П. П. Порфиров © 1935 P. P. Porfirov 1935 П. П. Порфиров P. P. Porfirov Эта статья доступна по лицензии Creative Commons Attribution 4.0 International (CC BY 4.0) This article is licensed under a Creative Commons Attribution 4.0 International License (CC BY 4.0) https://pmi.spmi.ru/pmi/article/view/15312

В работе по извлечению молибдена из руд, проводившейся НИСом Ленинградского Горного института, пришлось встретиться с вопросом выделения молибдена из растворов от выщелачивания. В виду того что электролитическое осаждение, при большей простоте опера­ций, дает продукт в виде кислородного соединения молибдена, свободного от других металлов и отличающегося большей чистотой, представляет большой практический интерес изучение процесса катодного осаждения гидроокиси молибдена из его растворов. В ниже описанных опытах мы экспериментально изучили ход процесса электролитического осаждения гидроокиси из растворов молибденовокислого аммония. Изучалось влияние различных факторов, как-то: концентрации молибдена в растворе, плотности тока, температуры, концентрации солей других металлов, на процесс осаждения гидроокиси. Приведенные результаты показывают, что для удовлетворительного катодного осаждения гидроокиси молибдена необходимо соблюдение ряда условий (см. статью).

In the work on the extraction of molybdenum from ores carried out by the Scientific Research Department of the Leningrad Mining Institute, the issue of recovering molybdenum from leaching solutions arose. Since electrolytic deposition, due to its greater operational simplicity, yields a product in the form of an oxygen compound of molybdenum that is free from other metals and distinguished by higher purity, it is of great practical interest to study the process of cathodic deposition of molybdenum hydroxide from its solutions. In the experiments described below, we experimentally studied the course of the process of electrolytic deposition of hydroxide from solutions of ammonium molybdate. The influence of various factors, such as the concentration of molybdenum in the solution, current density, temperature, and the concentration of salts of other metals, on the hydroxide deposition process was investigated. The presented results show that for satisfactory cathodic deposition of molybdenum hydroxide, a number of conditions must be observed (see the article).

 Ключевые слова - E. F. Smith и L. G. Kollock, «Journ. Am. Chem. Soc.», 1901, том 23, стр. 669. E. F. Smith and L. G. Kollock, Journ. Am. Chem. Soc., 1901, volume 23, page 669. E. F. Exner, «Journ. Am. Chem. Soc.», 1903, том 25, стр. 896. E. F. Exner, Journ. Am. Chem. Soc., 1903, volume 25, page 896. E. T. Wherry и E. F. Smith, «Journ. Am. Chem. Soc.», 1907, том 29, стр. 806. E. T. Wherry and E. F. Smith, Journ. Am. Chem. Soc., 1907, volume 29, page 806. A. Fischer и J. Weise, «Zeitschr. f. analyt. Chem.», 1912, том 51, стр. 537. A. Fischer and J. Weise, Zeitschr. f. analyt. Chem., 1912, volume 51, page 537.